Al Summan Metals, headquartered in Dubai, UAE, distinguishes itself as a premier manufacturer and supplier of high-quality metal products, especially Aluminium 2014 Forgings. Recognized for its precision engineering and advanced manufacturing techniques, the company upholds strict quality control to guarantee that its aluminium solutions comply with global standards. Al Summan Metals takes pride in supplying Aluminium 2014 Forgings that provide exceptional strength, wear resistance, and durability, making them ideal for demanding industrial applications. Serving industries such as aerospace, automotive, and heavy engineering, the company combines innovation with reliability, positioning itself as a trusted partner for clients seeking high-performance aluminium components that ensure both structural integrity and long-lasting performance in tough conditions.
Aluminium 2014 Forgings are primarily composed of aluminium with roughly 4.4–5.0% copper, together with trace amounts of magnesium, manganese, and silicon, which enhance their strength, hardness, and wear resistance. This alloy demonstrates impressive mechanical properties, featuring a tensile strength of around 350–450 MPa, yield strength of about 200–280 MPa, and elongation of 10–15%, depending on the temper. It also provides excellent fatigue resistance, toughness, and dimensional stability, making it well suited for applications that require durable and high-strength aluminium components.
Standards :ASTM B247, B247
Temper :T6 T651 T6511
Specification :DIN, ASTM, BS and every International Standard
Flat bar blocks :up to 27″ width and 15,000 lbs.
Cylinders and sleeves :up to 50″ maximum O.D. and 65″ maximum length
Discs and hubs :up to 50″ diameter and 20,000 lbs.
Rolled, hand forged or mandrel forged rings :up to 84″ maximum O.D. and 40″ maximum length
Rounds, shafts and step shafts :up to 144″ maximum length and 20,000 lbs.
| Aluminium 2014 | Fe | Si | Mg | Mn | Cu | Zn | Ti | Al |
| 0.7 | 0.50 – 1.20 | 0.2 – 0.8 | 0.4 – 1.2 | 3.9 – 5.0 | 0.25 | 0.15 | 93.5 |
| Material | Temper | Diameter (mm) | Tensile Strength min ((N/mm²) | Yield Strength (min) (N/mm²) | Elongation on 5.65 V (min) |
| 2014 Bar | T4 | <20 | 370 | 230 | 11 |
| 2014 Bar | T4 | 20-75 | 390 | 250 | 11 |
| 2014 Bar | T4 | 75-150 | 390 | 250 | 9 |
| 2014 Bar | T4 | 150-200 | 370 | 230 | 8 |
| 2014 Bar | T6510 | 20-75 | 480 | 435 | 7 |
| 2014 Bar | T6510 | 75-150 | 465 | 420 | 7 |
| 2014 Bar | T6510 | 150-200 | 435 | 390 | 7 |
| STANDARD | UNS | WERKSTOFF NR. | European Standard | BS (OLD) | ISO | USA (AA) | GERMANY (DIN) | IS | Canadian |
| Aluminium 2014 | A92014 | 3.1255 | EN AW-2014 | HE15 | AlCu4SiMg | 2014 | AlCuSiMn | 24345 | B26S |
Yes, Aluminum 2014 is well suited for high-temperature forging applications thanks to its excellent strength, thermal resistance, and good machinability, which make it ideal for aerospace and automotive components.
Aluminum 2014 delivers high strength, excellent machinability, good wear resistance, and superior performance under high-stress conditions, making it ideal for aerospace, automotive, and structural custom forgings.
These Aluminium 2014 Forgings are widely used in aerospace structures, automotive parts, heavy machinery, and defense equipment, owing to their high strength-to-weight ratio and wear resistance. They are ideal for aircraft fittings, gear housings, hydraulic components, and structural frameworks where durability and performance under pressure are critical. The alloy’s distinctive combination of strength, toughness, and reliability makes it a preferred choice for industries that require long-lasting, high-performance aluminium components able to withstand demanding operational conditions.
We provide products supplied with both mill test certificates and third-party test certificates, guaranteeing the highest standards of quality and compliance.